Synthetic resin roof tile
Hot-sale product in Xingfa Tile Industry Co.,Ltd, synthetic resin roof tile is refined by introducing advanced production equipment & technologies, choosing the super weather proof engineering resin. It has the remarkable characteristics of rich colors & long lasting life , beautiful model with strong stereoscopic sensation, light weight, heat-insulation, sound-insulation, corrosion resistance, fire retarding. Color last more than 10 years, with service life of 25 years.
Specification
Model | Royal 1050 |
Width | 1050mm |
Efficient width | 960mm |
Thickness | 2.0mm,2.3mm,2.5mm,2.8mm,3.0mm |
Length | Customized (times of unit length 219mm) |
Purlin distance | 660mm-880mm |
Applications | Villa. Residential roof etc. |
Surface finishing | Spot type, standard type. |
Middle layer finsihing | standard three layers, fiber mesh finishing. |
synthetic resin roof size
synthetic pvc roof color
ASA Synthetic resin Roof Tile Test Result From SGS
NO. | Test item | Test method | Result |
1 | Color persistence | ISO | |
2 | Muriatic acid | ISO175-2010 | No visible change |
3 | Sulfuric acid | ISO175-2010 | No visible change |
4 | Alkali resistance | ISO175-2010 | No visible change |
5 | Tensile strength | ISO 527-1:2012 and | 20.3MPa |
6 | Nominal tensile strain at break | ISO 527-1:2012 and | 13% |
7 | Flexural strength | ISO 178:2010/Amd.1:2013 | 41.3MPa |
8 | Impact resistance | GB/T 8814-2004 Section | -10℃,hammering,intact |
9 | Oxygen Index | ISO 4589-1:1996 and ISO | 32.80% |
10 | Burning test | DIN 4102-1:1998-05 | B1 |
ASA Synthetic resin Roof Tile Test Result From SGS (2014)
NO. | Test item | Test method | Test condition | Test result | |
1 | Xenon-arc Exposure | ISO 4892-2:2013,ISO 105-A02:1993 | ISO 4892-2:2013 cycle 4 Irradiance:(0.51±0.02)W/(m2·nm)@340nm 102min light at (63±3)℃BPT,(50±10)℃RH | Greyscale | 2-3 |
∆E*ab | 3.5 | ||||
2 | Thermal resistance | With reference to ASTM D3045-92(2010) and client’s requirements | 150℃.30min | Visible deformation and color fading, but o other visible change. | |
3 | Muriatic acid resistance | Medium: 35%(m/m) HCI(AR) | |||
4 | Sulfuric acid resistance | With reference to ISO 175-2010 and client’s requirements | Medium: 30%(m/m) H2SO4(AR) | No visisble change | |
5 | Alikali resistance | With reference to ISO 175-2010 and client’s requirements | Medium: 40% (m/m) NaOH(AR) | No visible change. | |
6 | Density | ISO 1183-1:2012 Method A | Abosolute alcohol, 23±0.5℃ | 1.799g/cm3 | |
7 | Flexural strength | ISO 178:2010/Amd.1:2013 | Specimen:100x10.96x3.12mm | 41.3MPa | |
8 | Flexural modulus | 4520MPa | |||
9 | Charpy unnotched impact strength | ISO 179-1: 2010 | Specimen: ISO 179-1/1Eu | 38Kj/M2 | |
10 | Vicat softening temperature | ISO 306:2004 Method B50 | Specimen thickness: 3.01mm | 77.3℃ | |
11 | Tensile strength | ISO 527-1:2012 and ISO 527-2:2012 | Specimen: Type 1B | 20.3MPa | |
12 | Nominal tensile strain at break | 13% | |||
13 | Impact resistance | GB/T 8814-2004 Section 5.7 and 6.7 | Precondition:-10℃,1h→ | Number of spcimen breakage:0 | |
14 | Dimensional change | With reference to ASTM D1204-08 and client’s requirement | Condition: 100℃,60min→ | X | -0.7% |
Y | -1.3% | ||||
15 | Oxygen Index | ISO 4589-1: 1996 and ISO 4589-2: 1996/Amd.1:2005 | Specimen: Type III | 32.8% | |
16 | Horizontal burning test | UL 94-2013 Section 7 | Specimen: 126x13.4x3.0mm | HB | |
17 | 20mm Vertiacal burning test | UL 94-2013 Section 8 | Specimen: 126x13.4x3.0mm | V-1 | |
18 | Burning test | DIN 4102-1:1998-05 | See appendix1 | The sample tested met the requirements of class B2 |
Contact
Supplier
Aluminum Composite Panels
Balustrades & Handrails
Bathroom
Boards
Building Glass
Ceilings
Countertops,Vanity Tops & Table Tops
Curtain Walls & Accessories
Decorative Films
Door & Window Accessories
Doors & Windows
Faucets, Mixers & Taps
Flooring & Accessories
Formwork
HVAC Systems & Parts
Kitchen
Ladders & Scaffoldings
Metal Building Materials
Mosaics
Plastic Building Materials
Quarry Stone & Slabs
Real Estate
Stairs & Stair Parts
Tiles & Accessories
Door, Window & Accessories
Stone