Sintered Ferrite Magnet is manufactured from oxide material by powder metallurgical process. Its advantages include: low cost, excellent corrosion resistance, resistance to be demagnetized etc. The normal working temperature of ferrite magnet is between -40°C and +250°C. It can be magnetized before or after assembly. Generally, sintered ferrite magnet can be machined to regular shapes like segment, blocks, rings and discs etc. The normal grade for sintered Ferrite magnets are Y10T, Y25, Y30, Y30BH, Y35 etc.
Electric Motors; Loudspeaker; Magnetic Knife Holder /Rack; General Holding Devices and so on
Injection ferrite magnet is made of compound of ferrite powder and Nylon. It is produced under magnetic field to achieve better magnetic orientation. The injection processing ensure magnets to have very complex shape and also ensure precise tolerance. Multi-poles magnetization can be achieved easily.
Electric Motors 、Loudspeaker 、Magnetic Knife Holder /Rack 、General Holding Devices and so on
MAGNETIC CHARACTERISTICS AND PHYSICAL PROPERTIES OF INJECTION FERRITE | |||||||||||
GRADE | Binder | Br | Hcb | Hcj | (BH)max | Mold density (g/cm3) | Melt flow rate | Flexual strength | Flexual modulus | ||
Gs | mT | Oe | Oe | MGOe | g/10min(MI) | condition | Mpa(kg/cm2) | Gpa(kg/cm2) | |||
DMS121-A | PA6 | 2900 | 290 | 2500 | 3100 | 2.1 | 3.65 | 100 | 270℃ 10kg | 157.1 | 26.8 |
DMS121-B | PA6 | 2850 | 285 | 2500 | 3150 | 1.95 | 3.6 | 70 | 270℃ 10kg | 165.5 | 25.9 |
DMS121-C | PA6 | 2750 | 275 | 2400 | 2900 | 1.8 | 3.53 | 60 | 270℃ 10kg | 145.8 | 20.1 |
DMS121-D | PA6 | 2550 | 255 | 2350 | 2800 | 1.6 | 3.45 | 60 | 270℃ 10kg | 154.7 | 22.3 |
DMS121-E | PA6 | 1225 | 122.5 | 1150 | 2150 | 0.37 | 2.3 | 150 | 270℃ 10kg | 120.5 | 28.6 |
DMS121-F | PA6 | 1550 | 155 | 1350 | 3100 | 0.64 | 2.55 | 140 | 270℃ 10kg | 115.8 | 27.8 |
DMS121-J | PA6 | 2850 | 285 | 2250 | 2600 | 2 | 3.6 | 70 | 270℃ 10kg | 160 | 26.2 |
DMS121-T | PA6 | 2300 | 230 | 2000 | 3000 | 1.5 | 3 | 80 | 270℃ 10kg | 139.8 | 27.5 |
DMS221-A | PA12 | 2750 | 275 | 2300 | 2400 | 1.85 | 3.4 | 60 | 270℃ 10kg | 162 | 25.2 |
DMS221-B | PA12 | 2820 | 282 | 2600 | 3300 | 2 | 3.6 | 50 | 270℃ 10kg | 162 | 25.2 |
MAGNETIC CHARACTERISTICS AND PHYSICAL PROPERTIES OF INJECTION FERRITE | ||||||||||||||||||
GRADE | Binder resin | Br | Hcb | Hcj | (BH)max | Mold density | Melt flow rate | Flexual strength | Flexual modulus | Tensile strength | Elangation | Impact strength | Shrinkage | |||||
Gs | mT | Oe | kA/m | Oe | kA/m | MGOe | Kj/m3 | (g/cm3) | g/10min(MI) | condition | Mpa(kg/cm2) | Gpa(kg/cm2) | Mpa | % | kj/m2 | % | ||
TP-S62 | PA6 | 2390 | 239 | 2140 | 170 | 2900 | 230.8 | 1.4 | 11.14 | 3.27 | 100 | 270℃ -10kg | 189 1927 | 15.8 1.6E+05 | 99.5 1015 | 4.6 | NB NB | 0.75 |
TP-S65 | PA6 | 2750 | 275 | 2350 | 187 | 2780 | 221.2 | 1.87 | 14.88 | 3.63 | 135 | 270℃ -10kg | 167 1703 | 23 2.3E+05 | 79.1 807 | 3.0 | 11.9 12.1 | 0.57 |
TP-S67K | PA6 | 2900 | 290 | 2280 | 180 | 2650 | 210.9 | 2.07 | 16.5 | 3.73 | 70 | 270℃ -10kg | 182 1856 | 27.5 2.8E+05 | 97.6 995 | 3.4 | 13.5 13.7 | 0.41 |
TP-F26S | PA12 | 2820 | 282 | 2360 | 188 | 2870 | 228.4 | 1.96 | 15.6 | 3.63 | 65 | 270℃ -10kg | 115 1173 | 14.5 1.5E+05 | 59.1 603 | 3.9 | 15.6 15.9 | 0.66 |
TP-A27E | PA12 | 2890 | 289 | 2390 | 190 | 2880 | 229.2 | 2.05 | 16.2 | 3.69 | 65 | 270℃ -10kg | 92 938 | 11.3 1.2E+05 | 45.6 465 | 5.3 | 20.4 20.8 | 0.72 |
TP-S76 | PPS | 2360 | 236 | 2160 | 172 | 3060 | 243 | 1.38 | 11 | 3.33 | 160 | 270℃ -10kg | 149 1522 | 13.9 1.4E+05 | 73.7 751 | 2.5 | 20.6 21.0 | 0.6 |
MAGNETIC CHARACTERISTICS AND PHYSICAL PROPERTIES OF INJECTION FERRITE | |||||||||||||||||
GRADE | Br | Hcb | Hcj | (BH)max | Mold density (g/cm3) | Melt flow rate | Moisture | Flexual strength | Tensile strength | Impact strength | Shrinkage | Heat distorsion temp. | Coefficent of linear expansion | ||||
Gs | mT | Oe | kA/m | Oe | kA/m | MGOe | Kj/m3 | g/10min | ppm | Mpa(kg/cm2) | Mpa | kj/m2 | % | ℃ | 1/℃ | ||
L240 | 4540 | 454 | 3830 | 305 | 8680 | 691 | 4.4 | 35 | 4.69 | 463 | 68 | 118.3 | 26.4 | 0.6 | 0.6 | 143 | 5.5OE-05 |
L250 | 5070 | 507 | 4250 | 338 | 8710 | 693 | 5.4 | 43 | 5.01 | 470 | 36 | 115 | 17.1 | 0.4 | 0.4 | 4.2OE-05 | |
L260 | 5563 | 556 | 4550 | 362 | 9010 | 717 | 6.3 | 50.1 | 5.37 | 477 | 50 | 96 | 10 | 0.4 | 0.4 | 3.80E-05 | |
L270 | 5815 | 582 | 4788 | 381 | 9028 | 718 | 6.9 | 54.9 | 5.57 | 216 | 60 | 93 | 11 | 0.5 | 0.5 | ||
N230 | 3940 | 394 | 3380 | 269 | 9860 | 785 | 3.3 | 26.3 | 3.97 | 468 | 31 | 120 | 37.1 | 0.9 | 0.9 | 7.10E-05 | |
N260 | 5360 | 536 | 4430 | 353 | 9700 | 773 | 5.9 | 47 | 5.02 | 412 | 28 | 121.4 | 17.1 | 0.5 | 0.5 | ||
N270 | 5850 | 585 | 4650 | 370 | 8920 | 710 | 6.8 | 54.1 | 5.28 | 505 | 46 | 114.3 | 13.1 | 0.4 | 0.4 | 151 | 3.50E-05 |
N280S | 6190 | 619 | 4840 | 385 | 8850 | 704 | 7.6 | 59.7 | 5.54 | 773 | 85 | 71.9 | 7.6 | 0.2 | 0.2 | 2.30E-05 |
Magnetic and Physical Properties for Sintered Ferrite magnet(Chinese Standard) | ||||
GRADE | Br(Gs) | Hcb(Oe) | HcJ(Oe) | (BH)max(MGOe) |
Y8T | 2000 - 2350 | 1570 - 2010 | 2640 - 3520 | 0.8 - 1.2 |
Y10T | >2000 | 1600 | 2640 | 0.81 |
Y20 | 3200 - 3800 | 1700 - 2390 | 1760 - 2450 | 2.3 - 2.8 |
Y22H | 3100 - 3600 | 2770 - 3140 | 3520 - 4020 | 2.5 - 3.0 |
Y23 | 3200 - 3700 | 2140 - 2390 | 2390 - 2890 | 2.5 - 3.2 |
Y25 | 3600 - 4000 | 1700 - 2140 | 1760 - 2510 | 2.8 - 3.5 |
Y26H | 3600 - 3900 | 2770 - 3140 | 2830 - 3200 | 2.9 - 3.5 |
Y27H | 3700 - 4000 | 2580 - 3140 | 2640 - 3200 | 2.9 - 3.5 |
Y28 | 3700 - 4000 | 2200 - 2640 | 2260 - 2770 | 3.3 - 3.8 |
Y30 | >3800 | 2400 | 2500 | 3.3 |
Y30BH | >3850 | 2800 | 2900 | 3.4 |
Y30H-1 | 3800 - 4000 | 2890 - 3455 | 2950 - 3640 | 3.4 - 4.1 |
Y30H-2 | 3950 - 4150 | 3460 - 3770 | 3900 - 4210 | 3.6 - 4.0 |
Y32 | 4000 - 4200 | 2010 - 2390 | 2070 - 2450 | 3.8 - 4.2 |
Y33 | 4100 - 4300 | 2770 - 3140 | 2830 - 3200 | 4.0 - 4.4 |
Y33H | >3850 | 3150 | 3250 | 3.7 |
Y35 | >4000 | 2600 | 2700 | 3.85 |
Y35BH | >4000 | >2952 | >3014 | 3.7 |
微波炉磁 | >4150 | 2800 | 2900 | 4.1 |
Magnetic and Physical Properties for Sintered Ferrite magnet(German Standard) | ||||
GRADE | Br(Gs) | Hcb(Oe) | HcJ(Oe) | (BH)max(MGOe) |
HF8/22 | 200-220 | 125-140 | 220-230 | 6.5-6.8 |
(2.00-2.20) | (1.57-1.76) | (2.76-2.89) | (0.8-1.1) | |
HF20/19 | 320-333 | 170-190 | 190-200 | 20.0-21.0 |
(3.20-3.33) | (2.14-2.39) | (2.39-2.51) | (2.5-2.7) | |
HF20/28 | 310-325 | 220-230 | 280-290 | 20.0-21.0 |
(3.10-3.25) | (2.76-2.89) | (3.20-3.64) | (2.5-2.7) | |
HF22/30 | 350-365 | 255-265 | 290-300 | 22.0-23.5 |
(3.50-3.65) | (3.20-3.33) | (3.64-3.77) | (2.8-3.0) | |
HF24/16 | 350-365 | 155-175 | 160-180 | 24.0-25.5 |
(3.50-3.65) | (1.95-2.20) | (2.01-2.26) | (3.0-3.2) | |
HF24/23 | 350-365 | 220-230 | 230-240 | 24.0-25.5 |
(3.50-3.65) | (2.76-2.89) | (2.89-3.01) | (3.0-3.2) | |
HF24/25 | 360-370 | 260-270 | 350-360 | 24.0-25.5 |
(3.60-3.70) | (3.27-3.39) | (4.40-4.52) | (3.0-3.2) | |
HF26/16 | 370-380 | 155-175 | 160-180 | 26.0-27.0 |
(3.70-3.80) | (1.95-2.20) | (2.01-2.26) | (3.2-3.4) | |
HF26/18 | 370-380 | 175-190 | 180-190 | 26.0-27.0 |
(3.70-3.80) | (2.20-2.39) | (2.26-2.39) | (3.3-3.4) | |
HF26/24 | 370-380 | 230-240 | 240-250 | 26.0-27.0 |
(3.70-3.80) | (2.89-3.01) | (3.01-3.14) | (3.3-3.4) | |
HF26/26 | 370-380 | 230-240 | 260-270 | 26.0-27.0 |
(3.70-3.80) | (2.89-3.01) | (3.27-3.39) | (3.3-3.4) | |
HF26/30 | 385-395 | 260-270 | 300-310 | 26.0-27.0 |
(3.85-3.95) | (3.27-3.39) | (3.77-3.89) | (3.3-3.4) | |
HF28/26 | 385-395 | 250-265 | 260-275 | 28.0-30.0 |
(3.85-3.95) | (3.14-3.33) | (3.27-3.45) | (3.5-3.8) | |
HF28/28 | 385-395 | 260-270 | 280-290 | 28.0-30.0 |
(3.85-3.95) | (3.27-3.39) | (3.50-3.60) | (3.5-3.8) | |
HF30/26 | 395-405 | 250-260 | 260-270 | 30.0-31.5 |
(3.95-4.05) | (3.14-3.33) | (3.27-3.39) | (13.8-3.9) | |
HF32/17 | 410-420 | 160-180 | 165-175 | 32.0-33.0 |
(4.10-4.20) | (2.01-2.26) | (2.07-2.20) | (4.0-4.1) | |
HF32/22 | 410-420 | 215-225 | 220-230 | 32.0-33.0 |
(4.10-4.20) | (2.70-2.83) | (2.76-2.89) | (4.0-4.1) | |
HF32/25 | 410-420 | 240-250 | 250-260 | 32.0-33.0 |
(4.10-4.20) | (3.01-3.14) | (3.14-3.27 | (4.0-4.1) |
Magnetic and Physical Properties for Sintered Ferrite magnet(American Standard) | ||||
GRADE | Br(Gs) | Hcb(Oe) | HcJ(Oe) | (BH)max(MGOe) |
C - 1 | 2300 | 1860 | 3500 | 1.05 |
C - 5 | 3800 | 2400 | 2500 | 3.40 |
C - 7 | 3400 | 3230 | 4000 | 2.75 |
C-8 | >3850 | 2950 | 3050 | 3.5 |
C - 8B | 4200 | 2913 | 2960 | 4.12 |
C - 8C | >4300 | 2500 | 2550 | 4.3 |
C - 9 | 3800 | 3516 | 4010 | 3.32 |
C - 10 | 4000 | 3617 | 3510 | 3.82 |
C - 11 | 4300 | 2512 | 2560 | 4.32 |
C - 12 | 3900 | 3667 | 3893 | 3.9 |
Magnetic and Physical Properties for Sintered Ferrite magnet(Japanese Standard) | ||||
GRADE | Br(Gs) | Hcb(Oe) | HcJ(Oe) | (BH)max(MGOe) |
FB9N | 4500 | 3355 | 3455 | 4.88 |
FB9B | 4400 | 4146 | 4347 | 4.65 |
FB9H | 4200 | 4008 | 4850 | 4.20 |
FB6N | 4300 | 3104 | 3154 | 4.41 |
FB6B | 4100 | 3656 | 3845 | 4.00 |
FB6H | 3900 | 3656 | 4347 | 3.60 |
FB6E | 3700 | 3505 | 4800 | 3.25 |
FB5N | 4300 | 2702 | 2727 | 4.41 |
FB5B | 4100 | 3154 | 3753 | 4.00 |
FB5H | 3950 | 3594 | 3907 | 3.70 |
FB4A | 4000 | 2000 | 2025 | 3.80 |
FB4D | 4000 | 2802 | 2853 | 3.74 |
FB3N | 3850 | 2802 | 2853 | 3.30 |
FB3G | 3600 | 3004 | 3154 | 2.95 |
FB1A | 2050 | 1798 | 3004 | 0.92 |