◪ Good bond ability and good mechanical properties
◪ Good over baking resistance,Excellent weatherability
◪ Good flowing and glossy
◪ Better storage capability than Polyester/TGIC type .
◪ Curing condition : 180℃/10min
Base: Thermoset powder coating based on polyester resins and hydroxylalkylamide resins.
Color: Various
Gloss Range: 15-95% (smooth surface at 60°)
Surface: Smooth and special finish (texture, wrinkle, hammer etc) for all kinds of gloss
Density: 1.4-1.8 g/cm3
Curing guide: 180℃/10min
Film characteristics: Good film appearance with the excellent mechanical and exterior exposure durability. These polyester coatings also exhibit excellent over baking resistance across a wide range of cure conditions.
Properties | Method | Value | |
Impact | GB/T 1732-1993 | ISO 6272 | 50kg.cm(Direct) |
Cupping test | GB/T 9753-1988 | ISO 1520 | ≥7mm |
Adhesion(Cross Cut) | GB/T 9286-1998 | ISO 2409 | 0 Grade |
Flexibility | GB/T 6742-1986 | ISO 1519 | 2mm |
Pencil Hardness | GB/T 6739-2006 | ASTM D3363 | H~2H |
Salt Spray | GB/T 1771-2007 | ISO 7253 | ≥500h |
Humidity | GB/T 1740-2007 | ISO 6270 | ≥1000h |
Weatherability | GB/T1865-1997 | ASTM G151 | 240h(QUV B313) |
All the tests are using 0.8mm cold-rolled sheets. Coating thickness: 50-80μm |